High Density Strata Wood ya Mafuta Transformer
Iwo m'malo mbale zitsulo, insulating makatoni, epoxy makatoni, etc. ntchito epoxy galasi nsalu bolodi mu mbali izi amachepetsa kudziona kulemera ndi chuma mtengo wa thiransifoma.Magetsi laminated board ndi veneer yopangidwa ndi mitengo yamtengo wapatali ya birch, yomwe imaphikidwa, kupukuta ndi kuuma.Pambuyo yokutidwa ndi guluu wapadera insulating, amapangidwa ndi kutentha ndi kuthamanga kwambiri.
Kukula kwakukulu kwa mbale (kutalika × m'lifupi × makulidwe): 4000×3000×120(mm)
Kufotokozera wamba ndi miyeso ya mbale (kutalika × m'lifupi × makulidwe): 3000×1500×(10—120) (mm), 2400×2000×(10—120) (mm)
Dzina | Magetsi insulating laminated nkhuni | |||||
Yesani chinthu | Chigawo | Tnjira est | ||||
ZowonekaKuchulukana | g/m3 | IEC 61061-2: 2001 | ||||
Chinyezi | % | |||||
mafuta adsorption | % | |||||
Kusiyanasiyana kwa makulidwekale ndipambuyo pa kuyamwa mafuta | % | |||||
Compressive mphamvu | zabwinobwino | Oyima mpaka zigawo | Mpa | Onani ku ISO 604: 1993 | ||
kufanana ndi zigawo | ||||||
90℃ | Oyima mpaka zigawo | |||||
kufanana ndi zigawo | ||||||
Flexural mphamvu | wabwinobwino | MD | Mpa | IEC 61061-2: 2001 | ||
CD | ||||||
90℃ | MD | Mpa | ||||
CD | ||||||
Flexural modulus | zabwinobwinocy | MD | Mpa | |||
CD | ||||||
90℃ | MD | |||||
CD | ||||||
Compressibilityperpendicularku kulaminations | C | % | ||||
C rev | ||||||
Mphamvu yamphamvu kufanana ndilaminations | Oyima mpaka zigawo | kj/m2 | ||||
kufanana ndi zigawo | ||||||
Kuipitsidwa kwamadzimadzi dmagetsi |
| |||||
Mphamvu zamagetsi perpendicularku kulaminations | MV/m | |||||
Mphamvu yamagetsi kufanana ndilaminations | KV | |||||
Kuchepa pambuyo kuyanika | Njira | % | ||||
Bmalangizo | ||||||
makulidwe |